- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.919
- 拉伸强度 [MPa]: 10.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ExxonMobil Method |
| Melt Flow | 0.25 g/10 min | 0.25 g/10 min | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 82 | 82 | 15s; ASTM D2240 |
| Hardness, Shore D | 38 | 38 | 15s; ASTM D2240 |
| Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
| Tensile Strength, Yield | 10.3 MPa | 1500 psi | at 2% Offset; ASTM D638 |
| Elongation at Break | 790 % | 790 % | ASTM D638 |
| Elongation at Yield | 38 % | 38 % | ASTM D638 |
| 1% Secant Modulus | 205 MPa | 29800 psi | ASTM D790 |
| Impact Test | 23.0 J | 17.0 ft-lb | Instrumented Impact Total Energy; ASTM D3763 |
| 29.8 J | 22.0 ft-lb | Instrumented Impact Total Energy at -40°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 91.7 °C | 197 °F | ASTM D1525 |