ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity

ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity 物性表: ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity物性表及特性介绍,ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity注塑参数详情,如需ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 2.0
  • 密度 [g/cm3]: 0.925
  • 透光率 [%]: 90.0
 
Physical PropertiesMetricEnglishComments
Density 0.925 g/cc0.0334 lb/in³Exxon Method
Thickness 31.8 microns1.25 mil
Melt Flow 2.0 g/10 min2.0 g/10 minExxon Method
 
Mechanical PropertiesMetricEnglishComments
Film Tensile Strength at Yield, MD 9.70 MPa1410 psiASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa1600 psiASTM D882
Film Elongation at Break, MD 200 %200 %ASTM D882
Film Elongation at Break, TD 500 %500 %ASTM D882
Secant Modulus, MD 0.210 GPa30.5 ksiASTM D882
Secant Modulus, TD 0.250 GPa36.3 ksiASTM D882
Elmendorf Tear Strength MD 150 g150 gASTM D1922
Elmendorf Tear Strength TD 350 g350 gASTM D1922
Elmendorf Tear Strength, MD 4.72 g/micron120 g/milASTM D1922
Elmendorf Tear Strength, TD 11.0 g/micron280 g/milASTM D1922
Dart Drop 2.20 g/micron56.0 g/milF50; ASTM D1709
Dart drop Test 70.0 g0.154 lbF50; ASTM D-1709
Film Tensile Strength at Break, MD 25.0 MPa3630 psiASTM D882
Film Tensile Strength at Break, TD 18.0 MPa2610 psiASTM D882
 
Thermal PropertiesMetricEnglishComments
Melting Point 113 °C235 °FExxon Method
 
Optical PropertiesMetricEnglishComments
Haze 5.0 %5.0 %ASTM D1003
Gloss 70 %70 %45°, ASTM D-2457
Transmission, Visible 90.0 %90.0 %clear; thickness not quantified

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-41472.html

免责声明: 本文 ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4