- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 140 % | 140 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Secant Modulus, MD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.260 GPa | 37.7 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 280 g | 280 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 90 g | 90 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 8.82 g/micron | 224 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.83 g/micron | 72.0 g/mil | ASTM D1922 |
| Dart Drop | 3.15 g/micron | 80.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 100 g | 0.221 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 109 °C | 228 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 65 % | 65 % | 45°, ASTM D-2457 |