- 熔体流动速率 [g/10min]: 70.0
- 密度 [g/cm3]: 0.913
- 拉伸强度 [MPa]: 8.96
- 脆化温度 [℃]: -43.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.913 g/cc | 0.0330 lb/in³ | ExxonMobil Method |
| Melt Flow | 70 g/10 min | 70 g/10 min | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48 | 48 | 15s; ASTM D2240 |
| Tensile Strength at Break | 7.58 MPa | 1100 psi | ASTM D638 |
| Tensile Strength, Yield | 8.96 MPa | 1300 psi | at 2% Offset; ASTM D638 |
| Film Elongation at Break, MD | 220 % | 220 % | ASTM D882 |
| 1% Secant Modulus | 1450 MPa | 210000 psi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 °C | 219 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 76.1 °C | 169 °F | ASTM D1525 |
| Brittleness Temperature | -43.9 °C | -47.0 °F | ASTM D746 |