- 熔体流动速率 [g/10min]: 40.0
- 密度 [g/cm3]: 0.922
- 拉伸强度 [MPa]: 12.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ExxonMobil Method |
| Melt Flow | 40 g/10 min | 40 g/10 min | at 190ºC/2.16 kg; ASTM D1238 |
| Slip Level | 550 ppm | 550 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 88 | 88 | 15s; ASTM D2240 |
| Hardness, Shore D | 43 | 43 | 15s; ASTM D2240 |
| Tensile Strength at Break | 7.58 MPa | 1100 psi | ASTM D638 |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D638 |
| Elongation at Break | 110 % | 110 % | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| 1% Secant Modulus | 276 MPa | 40100 psi | ASTM D790 |
| Impact Test | 19.0 J | 14.0 ft-lb | @ 73ºF, Instrumented Impact Total Energy; ASTM D3763 |
| 21.7 J | 16.0 ft-lb | @ 32ºF, Instrumented Impact Total Energy at 0°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 105 °C | 221 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 86.1 °C | 187 °F | ASTM D1525 |