- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | Exxon Method |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.8 MPa | 1570 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.5 MPa | 1670 psi | ASTM D882 |
| Film Elongation at Break, MD | 480 % | 480 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Secant Modulus, MD | 0.237 GPa | 34.4 ksi | ASTM D882 |
| Secant Modulus, TD | 0.246 GPa | 35.7 ksi | ASTM D882 |
| Coefficient of Friction | 0.69 | 0.69 | ASTM D1894 |
| Elmendorf Tear Strength MD | 190 g | 190 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 390 g | 390 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 9.37 g/micron | 238 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 19.2 g/micron | 488 g/mil | ASTM D1922 |
| Dart Drop | 22.2 g/micron | 563 g/mil | F50; ASTM D1709 |
| Dart drop Test | 450 g | 0.992 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 60.0 MPa | 8700 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 56.0 MPa | 8120 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 120 °C | 248 °F | Exxon Method |