- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | Exxon Method |
| Thickness | 76.2 microns | 3.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.80 MPa | 1280 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Break, MD | 620 % | 620 % | ASTM D882 |
| Film Elongation at Break, TD | 630 % | 630 % | ASTM D882 |
| Secant Modulus, MD | 0.205 GPa | 29.7 ksi | ASTM D882 |
| Secant Modulus, TD | 0.211 GPa | 30.6 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 930 g | 930 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1140 g | 1140 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 12.2 g/micron | 310 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 15.0 g/micron | 380 g/mil | ASTM D1922 |
| Dart Drop | >= 19.7 g/micron | >= 500 g/mil | F50; ASTM D1709 |
| Dart drop Test | >= 1500 g | >= 3.31 lb | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 57.0 MPa | 8270 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 55.0 MPa | 7980 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 119 °C | 246 °F | Exxon Method |