- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | Exxon Method |
| Thickness | 76.2 microns | 3.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.3 MPa | 1640 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.9 MPa | 1730 psi | ASTM D882 |
| Film Elongation at Break, MD | 630 % | 630 % | ASTM D882 |
| Film Elongation at Break, TD | 640 % | 640 % | ASTM D882 |
| Secant Modulus, MD | 0.293 GPa | 42.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.317 GPa | 46.0 ksi | ASTM D882 |
| Coefficient of Friction | 0.62 | 0.62 | ASTM D1894 |
| Elmendorf Tear Strength MD | 970 g | 970 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1240 g | 1240 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 12.7 g/micron | 323 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 16.3 g/micron | 413 g/mil | ASTM D1922 |
| Dart Drop | 9.96 g/micron | 253 g/mil | F50; ASTM D1709 |
| Dart drop Test | 760 g | 1.68 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 49.0 MPa | 7110 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 120 °C | 248 °F | Exxon Method |