- 熔体流动速率 [g/10min]: 0.28
- 密度 [g/cm3]: 0.921
- 拉伸强度 [MPa]: 10.0
- 弯曲强度 [MPa]: 16.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Melt Flow | 0.28 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.28 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| Dart drop Test | 190 g | 0.419 lb | ASTM D1709 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 98.9 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 16 % | 16 % | ASTM D1003 |