- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 11.0
- 弯曲强度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 54 | 54 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Elongation at Break | 375 % | 375 % | ASTM D638 |
| Modulus of Elasticity | 0.255 GPa | 37.0 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.207 GPa | 30.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.242 GPa | 35.1 ksi | ASTM D882 |
| Dart Drop | 1.77 g/micron | 45.0 g/mil | ASTM D1709 |
| Dart drop Test | 45.0 g | 0.0992 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 19.0 MPa | 2760 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Gloss | 63 % | 63 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 171 - 182 °C | 340 - 360 °F | |