- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.921
- 拉伸强度 [MPa]: 10.0
- 弯曲强度 [MPa]: 15.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Film Elongation at Break, MD | 325 % | 325 % | ASTM D882 |
| Film Elongation at Break, TD | 425 % | 425 % | ASTM D882 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Modulus of Elasticity | 0.221 GPa | 32.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.173 GPa | 25.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.221 GPa | 32.1 ksi | ASTM D882 |
| Dart Drop | 3.54 - 4.13 g/micron | 90.0 - 105 g/mil | ASTM D1709 |
| Dart drop Test | 90.0 - 105 g | 0.198 - 0.232 lb | ASTM D1709 |
| Film Tensile Strength at Break, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 91.0 °C | 196 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Gloss | 50 % | 50 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 171 - 182 °C | 340 - 360 °F | |