- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 12.0
- 弯曲强度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM D638 |
| Film Elongation at Break, MD | 315 % | 315 % | ASTM D882 |
| Film Elongation at Break, TD | 510 % | 510 % | ASTM D882 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Modulus of Elasticity | 0.297 GPa | 43.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.221 GPa | 32.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.262 GPa | 38.0 ksi | ASTM D882 |
| Dart Drop | 1.97 g/micron | 50.0 g/mil | ASTM D1709 |
| Dart drop Test | 50.0 g | 0.110 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.5 % | 4.5 % | ASTM D1003 |
| Gloss | 75 % | 75 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 163 - 174 °C | 325 - 345 °F | |