- 熔体流动速率 [g/10min]: 35.0
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 13.0
- 弯曲强度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Melt Flow | 35 g/10 min | 35 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Modulus of Elasticity | 0.345 GPa | 50.0 ksi | Secant; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |