- 熔体流动速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.93
- 拉伸强度 [MPa]: 14.0
- 弯曲强度 [MPa]: 13.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D1505 |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM D638 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Modulus of Elasticity | 0.483 GPa | 70.1 ksi | Secant; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 106 °C | 223 °F | ASTM D1525 |