- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.917
- 拉伸强度 [MPa]: 11.0
- 弯曲强度 [MPa]: 12.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Film Elongation at Break, MD | 280 % | 280 % | ASTM D882 |
| Film Elongation at Break, TD | 420 % | 420 % | ASTM D882 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Modulus of Elasticity | 0.173 GPa | 25.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.104 GPa | 15.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.138 GPa | 20.0 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 18.0 MPa | 2610 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 16.0 MPa | 2320 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 249 - 288 °C | 480 - 550 °F | |