- 熔体流动速率 [g/10min]: 4.5
- 密度 [g/cm3]: 0.923
- 拉伸强度 [MPa]: 12.0
- 弯曲强度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Melt Flow | 4.5 g/10 min | 4.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM D638 |
| Film Elongation at Break, MD | 250 % | 250 % | ASTM D882 |
| Film Elongation at Break, TD | 380 % | 380 % | ASTM D882 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Modulus of Elasticity | 0.290 GPa | 42.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.220 GPa | 31.9 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 14.0 MPa | 2030 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 93.0 °C | 199 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 249 - 288 °C | 480 - 550 °F | |