- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.917
- 拉伸强度 [MPa]: 9.0
- 弯曲强度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
| Film Elongation at Break, MD | 190 % | 190 % | ASTM D882 |
| Film Elongation at Break, TD | 280 % | 280 % | ASTM D882 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Modulus of Elasticity | 0.166 GPa | 24.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.0970 GPa | 14.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.145 GPa | 21.0 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 14.0 MPa | 2030 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 86.0 °C | 187 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 249 - 288 °C | 480 - 550 °F | |