- 熔体流动速率 [g/10min]: 14.0
- 密度 [g/cm3]: 0.916
- 拉伸强度 [MPa]: 8.0
- 弯曲强度 [MPa]: 9.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| Melt Flow | 14 g/10 min | 14 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 42 | 42 | ASTM D2240 |
| Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D638 |
| Film Elongation at Break, MD | 190 % | 190 % | ASTM D882 |
| Film Elongation at Break, TD | 220 % | 220 % | ASTM D882 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Modulus of Elasticity | 0.152 GPa | 22.0 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.0830 GPa | 12.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.124 GPa | 18.0 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 85.0 °C | 185 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 249 - 288 °C | 480 - 550 °F | |