- 熔体流动速率 [g/10min]: 0.43
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 - 0.922 g/cc | 0.0331 - 0.0333 lb/in³ | TSTM 209 B |
| Melt Flow | 0.43 - 0.57 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.43 - 0.57 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | >= 280 % | >= 280 % | ASTM D882 |
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 |
| Dart drop Test | >= 130 g | >= 0.287 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | >= 22.56 MPa | >= 3272 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 52.0 - 64.0 °C | 126 - 147 °F | HDT |
| Vicat Softening Point | 93.0 - 97.0 °C | 199 - 207 °F | ASTM D1525 |