- 熔体流动速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.925
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 0.925 g/cc | 0.0334 lb/in³ | ISO 1183 | ||
Melt Flow | 0.75 g/10 min | 0.75 g/10 min | ISO 1133 | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Stress | 12.0 MPa | 1740 psi | at Yield, TD; ISO R527-1 | ||
12.0 MPa | 1740 psi | at Yield, MD; ISO R527-1 | |||
Film Elongation at Break, MD | >= 200 % | >= 200 % | ISO R527-1 | ||
Film Elongation at Break, TD | >= 500 % | >= 500 % | ISO R527-1 | ||
Modulus of Elasticity | 0.190 GPa | 27.6 ksi | MD; ISO R527-1 | ||
0.200 GPa | 29.0 ksi | TD; ISO R527-1 | |||
Tensile Impact | 200 J/cm | 375 ft-lb/in | ASTM D4272 | ||
Coefficient of Friction | 0.70 | 0.70 | ASTM D1894 | ||
Tear Strength | 30.0 kN/m | 171 pli | TD; ISO 6383-2 | ||
35.0 kN/m | 200 pli | MD; ISO 6383-2 | |||
Film Tensile Strength at Break, MD | 28.0 MPa | 4060 psi | ISO R527-1 | ||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO R527-1 | ||
Optical Properties | Metric | English | Comments | ||
Haze | 10 % | 10 % | ASTM D1003A | ||
Gloss | 50 % | 50 % | ASTM D2457 | ||
Descriptive Properties | |||||
Clarity, mV | 34 | Sabtec |