- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.92
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.920 g/cc | 0.0332 lb/in³ | TSTM 209 B |
Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Tensile Stress | 15.7 MPa | 2280 psi | at Break, MD; ASTM D882 |
Elongation at Break | >= 330 % | >= 330 % | ASTM D882, MD |
>= 600 % | >= 600 % | ASTM D882, TD | |
Dart drop Test | 100 g | 0.221 lb | ASTM D1709 |
Thermal Properties | Metric | English | Comments |
Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
Optical Properties | Metric | English | Comments |
Haze | 15 % | 15 % | ASTM D1003A |
Gloss | 60 % | 60 % | ASTM D523 |
Processing Properties | Metric | English | Comments |
Melt Temperature | 160 - 180 °C | 320 - 356 °F |