- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ISO 1183 | ||
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 11.0 MPa | 1600 psi | at Yield, TD; ISO R527-1 | ||
| 12.0 MPa | 1740 psi | at Yield, MD; ISO R527-1 | |||
| Film Elongation at Break, MD | >= 200 % | >= 200 % | ISO R527-1 | ||
| Film Elongation at Break, TD | >= 500 % | >= 500 % | ISO R527-1 | ||
| Modulus of Elasticity | 0.180 GPa | 26.1 ksi | MD; ISO R527-1 | ||
| 0.190 GPa | 27.6 ksi | TD; ISO R527-1 | |||
| Tensile Impact | 350 J/cm | 656 ft-lb/in | ASTM D4272 | ||
| Coefficient of Friction | 0.70 | 0.70 | ASTM D1894 | ||
| Tear Strength | 20.0 kN/m | 114 pli | MD; ISO 6383-2 | ||
| 25.0 kN/m | 143 pli | TD; ISO 6383-2 | |||
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | ISO R527-1 | ||
| Film Tensile Strength at Break, TD | 26.0 MPa | 3770 psi | ISO R527-1 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 15 % | 15 % | ASTM D1003A | ||
| Gloss | 39 % | 39 % | ASTM D2457 | ||
| Descriptive Properties | |||||
| Clarity, mV | 56 | Sabtec | |||