- 熔体流动速率 [g/10min]: 0.4
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ASTM D1505 | ||
| Water Vapor Transmission | 10.0 g/m²/day | 0.644 g/100 in²/day | |||
| Oxygen Transmission Rate | 2000 cc/m²/day | 129 cc/100 in²/day | |||
| Nitrogen Transmission | 3500 cc-mm/m²-24hr-atm | 8890 cc-mil/100 in²-24hr-atm | |||
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50; ASTM D1693 | ||
| Thickness | 20.0 - 100 microns | 0.787 - 3.94 mil | |||
| 50.0 - 300 microns | 1.97 - 11.8 mil | ||||
| Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.40 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 | ||
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 | ||
| Tear Strength | 363 kN/m | 2070 pli | MD; ASTM D1922 | ||
| 373 kN/m | 2130 pli | TD; ASTM D1922 | |||
| Dart drop Test | 300 g | 0.662 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 23.5 MPa | 3410 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 22.6 MPa | 3280 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 110 °C | 230 °F | DSC | ||
| Crystallization Temperature | 104 °C | 219 °F | ASTM D1525 | ||
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D740 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 17 % | 17 % | ASTM D1003 | ||
| Gloss | 95 % | 95 % | 60°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 190 - 220 °C | 374 - 428 °F | |||
| Blow-up Ratio (BUR) | 1.5 - 2.0 | 1.5 - 2.0 | |||
| Descriptive Properties | |||||
| Slip Coefficient | 0.47 | ASMT D1894 | |||