- 熔体流动速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.924
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D792 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.5 MPa | 1670 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.5 MPa | 1670 psi | ASTM D882 |
| Film Elongation at Yield, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Yield, TD | 535 % | 535 % | ASTM D882 |
| Coefficient of Friction | >= 0.40 | >= 0.40 | ASTM D1894 |
| Elmendorf Tear Strength MD | 200 g | 200 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 290 g | 290 g | ASTM D1922 |
| Dart drop Test | 107 g | 0.236 lb | F50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 |
| 1% Secant Modulus, MD | 210 MPa | 30500 psi | ASTM D882 |
| 1% Secant Modulus, TD | 230 MPa | 33300 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 75 % | 75 % | at 45°; ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |