- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.912
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.912 g/cc | 0.0329 lb/in³ | ASTM D792 |
| Thickness | 51.0 microns | 2.01 mil | |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 7.38 MPa | 1070 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.38 MPa | 1070 psi | ASTM D882 |
| Film Elongation at Yield, MD | 640 % | 640 % | ASTM D638 |
| Film Elongation at Yield, TD | 890 % | 890 % | ASTM D882 |
| Puncture Energy | 3.162 J | 2.332 ft-lb | Low Friction Puncture |
| Elmendorf Tear Strength MD | 710 g | 710 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1010 g | 1010 g | ASTM D1922 |
| Dart drop Test | >= 1000 g | >= 2.20 lb | ASTM D1709/A |
| Film Tensile Strength at Break, MD | 49.0 MPa | 7110 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 54.0 MPa | 7830 psi | ASTM D882 |
| 1% Secant Modulus, MD | 114.0 MPa | 16530 psi | ASTM D882 |
| 1% Secant Modulus, TD | 123.0 MPa | 17840 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 72.0 °C | 162 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 8.7 % | 8.7 % | ASTM D1003 |
| Gloss | 63 % | 63 % | at 45°; ASTM D2457 |