- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.955
- 缺口冲击强度: 0.534
- 拉伸强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 0.800
- 硬度: 52.0
- 热变形温度 [℃]: 47.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 52 | 52 | ASTM D785 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | 300 % | 300 % | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 1.100 GPa | 159.5 ksi | ASTM D638 |
| Flexural Strength | 22.0 MPa | 3190 psi | ASTM D790 |
| Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 47.2 °C | 117 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | |