- 熔体流动速率 [g/10min]: 0.1
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 24.99
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | Base Resin; ISO 1183/ISO 1872-2B |
| 0.960 g/cc | 0.0347 lb/in³ | Compound; ISO 1183/ISO 1872-2B | |
| ESCR 10% Igepal® | >= 10000 hour | >= 10000 hour | ASTM D1693-A |
| Carbon Black Loading | 2.0 % | 2.0 % | ASTM D1603 |
| Melt Flow | >= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C | >= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 0.25 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.25 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ISO 868 |
| Tensile Strength, Yield | 24.99 MPa | 3625 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | >= 600 % | >= 600 % | ISO 527-2 |
| Charpy Impact, Notched | 1.60 J/cm² @Temperature 0.000 °C | 7.61 ft-lb/in² @Temperature 32.0 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Die Temperature | 200 - 210 °C | 392 - 410 °F | |
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | |
| Head Temperature | 200 - 210 °C | 392 - 410 °F | |