- 密度 [g/cm3]: 0.944
- 拉伸强度 [MPa]: 18.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in³ | Base Resin; ISO 1183 |
| 0.955 g/cc | 0.0345 lb/in³ | Compound; ISO 1183 | |
| Carbon Black Loading | 2.2 % | 2.2 % | ASTM D1603 |
| High Load Melt Index | 7.5 g/10 min @Load 21.6 kg, Temperature 190 °C | 7.5 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 18.0000 MPa | 2610.68 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | >= 600 % | >= 600 % | ISO 527-2 |