- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.956
- 热变形温度 [℃]: 70.0
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in³ | ISO 1183 |
| Oxidative Induction Time (OIT) | >= 15 min @Temperature 210 °C | >= 15 min @Temperature 410 °F | EN 728 |
| Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.30 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ISO 868 |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature 0.000 °C | 6.66 ft-lb/in² @Temperature 32.0 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75-2 |
| Vicat Softening Point | 72.0 °C @Load 5.10 kg | 162 °F @Load 11.2 lb | B50; ISO 306 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 180 - 210 °C | 356 - 410 °F | cylinder |
| Die Temperature | 200 - 210 °C | 392 - 410 °F | |
| Melt Temperature | 200 - 210 °C | 392 - 410 °F | |
| Head Temperature | 200 - 210 °C | 392 - 410 °F | |