- 熔体流动速率 [g/10min]: 0.33
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.952 g/cc | 0.952 g/cc | ASTM D1505/D792 |
| Thickness | 12.5 microns | 0.492 mil | |
| Melt Flow | 0.33 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.33 g/10 min @Load 11.0 lb, Temperature 374 °F | ASTM D1238 |
| 9.3 g/10 min @Load 21.6 kg, Temperature 190 °C | 9.3 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 620 % | 620 % | ASTM D882 |
| Film Elongation at Break, TD | 680 % | 680 % | ASTM D882 |
| Elmendorf Tear Strength MD | 6.0 g | 6.0 g | gF; ASTM D1922 |
| Elmendorf Tear Strength TD | 60 g | 60 g | gF; ASTM D1922 |
| Dart drop Test | 210 g | 0.463 lb | g/F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 50.0 MPa | 7250 psi | ASTM D882 |