- 熔体流动速率 [g/10min]: 0.33
- 密度 [g/cm3]: 0.962
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 1.439
- 热变形温度 [℃]: 72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 16 hour @Thickness 3.00 mm, Temperature 23.0 °C | 16 hour @Thickness 0.118 in, Temperature 73.4 °F | compression molded plaques; ASTM D1693B |
| Melt Flow | 0.33 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.33 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| High Load Melt Index | 45 g/10 min @Load 21.6 kg, Temperature 190 °C | 45 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
| Flexural Modulus | 1.439 GPa | 208.7 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |