- 熔体流动速率 [g/10min]: 4.9
- 密度 [g/cm3]: 0.943
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.943 g/cc | 0.0341 lb/in³ | ASTM-D792 |
| Melt Flow | 4.9 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.9 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 1320 % | 1320 % | ASTM-D882 |
| Film Elongation at Break, TD | 740 % | 740 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 20 g | 20 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 30 g | 30 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 0.800 g/micron | 20.3 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 1.20 g/micron | 30.5 g/mil | ASTM-D1922 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 450 MPa | 65300 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 160 MPa | 23200 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 75 % | 75 % | ASTM-D1003 |
| Gloss | 12 % | 12 % | Angle 60°; ASTM-D2457 |