- 熔体流动速率 [g/10min]: 0.6
- 密度 [g/cm3]: 0.951
- 缺口冲击强度: 1.0
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 980
- 热变形温度 [℃]: 66.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM-D792 |
| Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.60 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 56 | 56 | ASTM-D2240 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM-D638 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM-D638 |
| Elongation at Break | 2044 % | 2044 % | ASTM-D638 |
| Elongation at Yield | 12 % | 12 % | ASTM-D638 |
| Flexural Modulus, 1% Secant | 980 MPa | 142000 psi | ASTM-D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM-D648 |
| Vicat Softening Point | 125 °C @Load 1.02 kg | 257 °F @Load 2.25 lb | ASTM-D1525 |