- 熔体流动速率 [g/10min]: 0.65
- 密度 [g/cm3]: 0.961
- 缺口冲击强度: 1.2
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1260
- 热变形温度 [℃]: 79.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.961 g/cc | 0.0347 lb/in³ | ASTM-D792 |
| ESCR 100% Igepal® | 20 hour @Thickness 2.00 mm, Temperature 50.0 °C | 20 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| ESCR 10% Igepal® | 16 hour @Thickness 2.00 mm, Temperature 50.0 °C | 16 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 0.65 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.65 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| 40 g/10 min @Load 21.6 kg, Temperature 190 °C | 40 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM-D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM-D2240 |
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM-D638 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM-D638 |
| Flexural Modulus, 1% Secant | 1260 MPa | 183000 psi | ASTM-D790 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 °C | 174 °F | ASTM-D648 |
| Vicat Softening Point | 128 °C @Load 1.02 kg | 262 °F @Load 2.25 lb | ASTM-D1525 |