- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.948
- 拉伸强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 1280
- 热变形温度 [℃]: 76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM-D792 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM-D2240 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ASTM-D638 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM-D638 |
| Flexural Modulus, 1% Secant | 1280 MPa | 186000 psi | ASTM-D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | ASTM-D648 |
| Vicat Softening Point | 128 °C @Load 1.02 kg | 262 °F @Load 2.25 lb | ASTM-D1525 |