- 熔体流动速率 [g/10min]: 0.34
- 密度 [g/cm3]: 0.961
- 缺口冲击强度: 2.1
- 拉伸强度 [MPa]: 32.0
- 弯曲模量 [MPa]: 1210
- 热变形温度 [℃]: 79.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.961 g/cc | 0.0347 lb/in³ | ASTM-D792 |
| ESCR 100% Igepal® | 19 hour @Thickness 2.00 mm, Temperature 50.0 °C | 19 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| ESCR 10% Igepal® | 17 hour @Thickness 2.00 mm, Temperature 50.0 °C | 17 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 0.34 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.34 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| 28 g/10 min @Load 21.6 kg, Temperature 190 °C | 28 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM-D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | ASTM-D2240 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM-D638 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM-D638 |
| Flexural Modulus, 1% Secant | 1210 MPa | 175000 psi | ASTM-D790 |
| Izod Impact, Notched | 2.10 J/cm | 3.93 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 °C | 174 °F | ASTM-D648 |
| Vicat Softening Point | 129 °C @Load 1.02 kg | 264 °F @Load 2.25 lb | ASTM-D1525 |