- 熔体流动速率 [g/10min]: 2.2
- 密度 [g/cm3]: 0.952
- 缺口冲击强度: 1.1
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 990
- 热变形温度 [℃]: 68.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM-D792 |
| ESCR 10% Igepal® | <= 4.0 hour @Thickness 2.00 mm, Temperature 50.0 °C | <= 4.0 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ASTM-D2240 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM-D638 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM-D638 |
| Flexural Modulus, 1% Secant | 990 MPa | 144000 psi | ASTM-D790 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM-D648 |
| Vicat Softening Point | 125 °C @Load 1.02 kg | 257 °F @Load 2.25 lb | ASTM-D1525 |