- 熔体流动速率 [g/10min]: 11.0
- 密度 [g/cm3]: 0.96
- 拉伸强度 [MPa]: 29.0
- 弯曲模量 [MPa]: 1.65
- 热变形温度 [℃]: 91.0
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 30 hour | 30 hour | Condition B; ASTM D1693 |
| 60 hour | 60 hour | Condition A; ASTM D1693 | |
| Melt Flow | 11 g/10 min | 11 g/10 min | Condition 190/21.6, HLMI; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | 750 % | 750 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 1.65 GPa | 239 ksi | Tangent, 16:1 span:depth,0.5in/min; ASTM D790 |
| Tensile Impact Strength | 240 kJ/m² | 114 ft-lb/in² | Type S bar; ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Method A; ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | Loading 1, Rate A; ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A, type 1 specimen; ASTM D746 |