- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.945
- 拉伸强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 1.034
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D1505 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D683 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Flexural Modulus | 1.034 GPa | 150.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |