- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.942
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | ASTM D1505 | ||
| Moisture Vapor Transmission | 0.260 cc-mm/m²-24hr-atm | 0.660 cc-mil/100 in²-24hr-atm | ASTM F1249 | ||
| Oxygen Transmission | 138 cc-mm/m²-24hr-atm | 351 cc-mil/100 in²-24hr-atm | ASTM D3985 | ||
| Thickness | 25.4 microns | 1.00 mil | |||
| Melt Flow | 0.80 g/10 min | 0.80 g/10 min | ASTM D1238E | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 44.1 MPa | 6400 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 32.23 MPa | 4675 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 369 % | 369 % | ASTM D882 | ||
| Film Elongation at Break, TD | 626 % | 626 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 0.472 g/micron | 12.0 g/mil | Notched; ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 30.5 g/micron | 775 g/mil | Notched; ASTM D1992 | ||
| Dart Drop | <= 1.97 g/micron | <= 50.0 g/mil | ASTM D1709 | ||
| 1% Secant Modulus, MD | 614 MPa | 89000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 1100 MPa | 159000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.0 % | 7.0 % | ASTM D1003 | ||
| Gloss | 75 % | 75 % | 45°; ASTM D2457 | ||
| 127 % | 127 % | 60°; ASTM D2457 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 204 - 221 °C | 399 - 430 °F | |||
| Die Opening | 0.200 cm | 0.0787 in | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.