- 熔体流动速率 [g/10min]: 18.0
- 密度 [g/cm3]: 0.955
- 拉伸强度 [MPa]: 27.5
- 弯曲模量 [MPa]: 1.378
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| Melt Flow | 18 g/10 min | 18 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.5 MPa | 3990 psi | ASTM D683 |
| Elongation at Break | 125 % | 125 % | ASTM D638 |
| Flexural Modulus | 1.378 GPa | 199.9 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |