- 熔体流动速率 [g/10min]: 0.27
- 密度 [g/cm3]: 0.946
- 拉伸强度 [MPa]: 27.6
- 弯曲模量 [MPa]: 0.900
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in³ | ASTM D1505 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in³ | ASTM D1895 |
| Melt Flow | 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.27 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Flexural Modulus | 0.900 GPa | 131 ksi | 3 pt. secant. ASTM D790 |
| Tensile Impact Strength | 159 kJ/m² | 75.7 ft-lb/in² | S Bar; ASTM D 1822 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |