- 熔体流动速率 [g/10min]: 0.34
- 密度 [g/cm3]: 0.952
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Moisture Vapor Transmission | 0.140 cc-mm/m²-24hr-atm | 0.356 cc-mil/100 in²-24hr-atm | ASTM F1249 |
| Melt Flow | 0.34 g/10 min | 0.34 g/10 min | Condition E; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 460 % | 460 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Secant Modulus, MD | 0.710 GPa | 103 ksi | ASTM D882 |
| Secant Modulus, TD | 0.830 GPa | 120 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.630 g/micron | 16.0 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 15.7 g/micron | 400 g/mil | ASTM D1922 |
| Dart Drop | 3.50 g/micron | 88.9 g/mil | 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 51.0 MPa | 7400 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 43.0 MPa | 6240 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 221 °C | 430 °F | |