- 熔体流动速率 [g/10min]: 0.17
- 密度 [g/cm3]: 0.945
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D1505 |
| Moisture Vapor Transmission | 0.160 cc-mm/m²-24hr-atm | 0.406 cc-mil/100 in²-24hr-atm | ASTM F1249 |
| Melt Flow | 0.17 g/10 min | 0.17 g/10 min | Condition E; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 450 % | 450 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Secant Modulus, MD | 0.620 GPa | 89.9 ksi | ASTM D882 |
| Secant Modulus, TD | 0.760 GPa | 110 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.591 g/micron | 15.0 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 23.2 g/micron | 590 g/mil | ASTM D1922 |
| Dart Drop | 3.30 g/micron | 83.8 g/mil | 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 43.0 MPa | 6240 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 221 °C | 430 °F | |