- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.962
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | ASTM D1505 |
| Moisture Vapor Transmission | 0.100 cc-mm/m²-24hr-atm | 0.254 cc-mil/100 in²-24hr-atm | ASTM F1249 |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | Condition E; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 490 % | 490 % | ASTM D882 |
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 |
| Secant Modulus, MD | 1.10 GPa | 160 ksi | ASTM D882 |
| Secant Modulus, TD | 1.20 GPa | 174 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.748 g/micron | 19.0 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 8.27 g/micron | 210 g/mil | ASTM D1922 |
| Dart Drop | 1.40 g/micron | 35.6 g/mil | 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 26.0 MPa | 3770 psi | ASTM D882 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 °C | 410 °F | |