- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.939
- 拉伸强度 [MPa]: 21.0
- 弯曲强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 0.660
- 脆化温度 [℃]: -59.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 2000 hour @Temperature 50.0 °C | >= 2000 hour @Temperature 122 °F | F50, Cond. B.; ASTM D1693 |
| Melt Flow | 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.25 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| High Load Melt Index | 21 g/10 min @Load 21.6 kg, Temperature 190 °C | 21 g/10 min @Load 47.6 lb, Temperature 374 °F | High Load Melt Index; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Film Elongation at Break, MD | 370 % | 370 % | ASTM D882 |
| 580 % | 580 % | ASTM D882 | |
| Elongation at Break | >= 800 % | >= 800 % | Molded; ASTM D638 |
| Flexural Modulus | 0.660 GPa | 95.7 ksi | 3 pt. secant. ASTM D790 |
| Secant Modulus, MD | 0.410 GPa | 59.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.480 GPa | 69.6 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 1.18 g/micron | 30.0 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 27.2 g/micron | 690 g/mil | ASTM D1922 |
| Dart Drop | 7.50 g/micron | 191 g/mil | F50; 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 48.0 MPa | 6960 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 121 °C | 250 °F | ASTM D1525 |
| Brittleness Temperature | <= -59.0 °C | <= -74.2 °F | ASTM D746 |