- 密度 [g/cm3]: 0.96
- 弯曲强度 [MPa]: 30.3
- 弯曲模量 [MPa]: 1.52
- 热变形温度 [℃]: 77.8
- 脆化温度 [℃]: -7.78
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 25 hour | 25 hour | F50; ASTM D1693 |
| >= 500 hour | >= 500 hour | F50; ASTM D2561 | |
| Melt Index of Compound | 0.70 g/10 min | 0.70 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength, Ultimate | 30.3 MPa | 4400 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 1.52 GPa | 220 ksi | ASTM D790 |
| Tensile Impact | 53.4 J/cm | 100 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.8 °C | 172 °F | ASTM D648 |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |
| Brittleness Temperature | <= -7.78 °C | <= 18.0 °F | ASTM D746 |