- 密度 [g/cm3]: 0.948
- 拉伸强度 [MPa]: 24.8
- 弯曲模量 [MPa]: 1.01
- 热变形温度 [℃]: 67.8
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | 40 hour @Temperature 50.0 °C | 40 hour @Temperature 122 °F | F50; Molded and tested in accordance with ASTM D4976; ASTM D1693 |
| Melt Index of Compound | 5.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 54 | 54 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 26.2 MPa | 3800 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 1200 % | 1200 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 1.01 GPa | 146 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 105 kJ/m² | 50.0 ft-lb/in² | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 130 °C | 266 °F | Dow Method (DSC) |
| Crystallization Temperature | 118 °C | 244 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |