- 密度 [g/cm3]: 0.951
- 拉伸强度 [MPa]: 26.9
- 弯曲模量 [MPa]: 1.02
- 热变形温度 [℃]: 71.1
- 脆化温度 [℃]: -72.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D792 |
| Melt Index of Compound | 44 g/10 min @Load 2.16 kg, Temperature 190 °C | 44 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 26.9 MPa | 3900 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 26.9 MPa | 3900 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 10 % | 10 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 1.02 GPa | 148 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 84.0 kJ/m² | 40.0 ft-lb/in² | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128 °C | 262 °F | Dow Method (DSC) |
| Crystallization Temperature | 116 °C | 241 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | -72.2 °C | -98.0 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |