- 密度 [g/cm3]: 0.953
- 拉伸强度 [MPa]: 26.9
- 弯曲模量 [MPa]: 1.00
- 热变形温度 [℃]: 72.8
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | 80 hour @Temperature 50.0 °C | 80 hour @Temperature 122 °F | F50; Molded and tested in accordance with ASTM D4976; ASTM D1693 |
| High Load Melt Index | 33 g/10 min @Load 21.6 kg, Temperature 190 °C | 33 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Melt Index of Compound | 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.38 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 31.0 MPa | 4500 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 26.9 MPa | 3900 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 1.00 GPa | 145 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 168 kJ/m² | 80.0 ft-lb/in² | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131 °C | 268 °F | Dow Method (DSC) |
| Crystallization Temperature | 118 °C | 244 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.8 °C | 163 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 129 °C | 264 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |